牌号:PPO/PPE ;ZM035
属性-PROPERTIES |
典型值- TYPICAL VALUES |
单位-UNITS |
测试方法-TEST METHOD |
物性-PHYSICAL |
|
|
|
外观-Physical Form |
白色粉体-White Powder |
|
ZhongMu Method |
平均粒径-Mean Particle Size |
200 |
μm |
ZhongMu Method |
堆密度-Bulk Density |
0.4~0.5 |
g/cm3 |
ZhongMu Method |
特性黏度-Intrinsic Viscosity |
0.35±0.02 |
dl/g |
ZhongMu Method |
分子量-Molecuar weight |
22000~28000 |
|
ZhongMu Method |
挥发物-Volatiles |
<0.5 |
% |
ZhongMu Method |
甲苯含量-Toluene Content |
<1500 |
ppm |
ZhongMu Method |
铜含量-Copper Content |
<10 |
ppm |
ZhongMu Method |
熔融指数-Melt Index |
40~70(低熔融指数)70~90(中熔融指数) |
( 315 ℃, 10Kg) g/10min |
ZhongMu Method |
热性能-Thermal Properties |
|
|
|
玻璃化温度-Tg (half width) |
210 |
℃ |
ZhongMu Method |
牌号:PPO/PPE ;ZM040
属性-PROPERTIES |
典型值- TYPICAL VALUES |
单位-UNITS |
测试方法-TEST METHOD |
物性-PHYSICAL |
|
|
|
外观-Physical Form |
白色粉体-White Powder |
|
ZhongMu Method |
平均粒径-Mean Particle Size |
200 |
μm |
ZhongMu Method |
堆密度-Bulk Density |
0.4~0.5 |
g/cm3 |
ZhongMu Method |
特性黏度-Intrinsic Viscosity |
0.40±0.02 |
dl/g |
ZhongMu Method |
分子量-Molecuar weight |
30000~37000 |
|
ZhongMu Method |
挥发物-Volatiles |
<0.5 |
% |
ZhongMu Method |
甲苯含量-Toluene Content |
<1500 |
ppm |
ZhongMu Method |
铜含量-Copper Content |
<10 |
ppm |
ZhongMu Method |
熔融指数-Melt Index |
20~40 |
( 315 ℃, 10Kg) g/10min |
ZhongMu Method |
热性能-Thermal Properties |
|
|
|
玻璃化温度-Tg (half width) |
212 |
℃ |
ZhongMu Method |
牌号:PPO/PPE ;ZM045
属性-PROPERTIES |
典型值- TYPICAL VALUES |
单位-UNITS |
测试方法-TEST METHOD |
物性-PHYSICAL |
|
|
|
外观-Physical Form |
白色粉体-White Powder |
|
ZhongMu Method |
平均粒径-Mean Particle Size |
200 |
μm |
ZhongMu Method |
堆密度-Bulk Density |
0.4~0.5 |
g/cm3 |
ZhongMu Method |
特性黏度-Intrinsic Viscosity |
0.45±0.02 |
dl/g |
ZhongMu Method |
分子量-Molecuar weight |
39000~46000 |
|
ZhongMu Method |
挥发物-Volatiles |
<0.5 |
% |
ZhongMu Method |
甲苯含量-Toluene Content |
<1500 |
ppm |
ZhongMu Method |
铜含量-Copper Content |
<10 |
ppm |
ZhongMu Method |
熔融指数-Melt Index |
10~20 |
( 315 ℃, 10Kg) g/10min |
ZhongMu Method |
热性能-Thermal Properties |
|
|
|
玻璃化温度-Tg (half width) |
213 |
℃ |
ZhongMu Method |
牌号:PPO/PPE ;ZM050
属性-PROPERTIES |
典型值- TYPICAL VALUES |
单位-UNITS |
测试方法-TEST METHOD |
物性-PHYSICAL |
|
|
|
外观-Physical Form |
白色粉体-White Powder |
|
ZhongMu Method |
平均粒径-Mean Particle Size |
200 |
μm |
ZhongMu Method |
堆密度-Bulk Density |
0.4~0.5 |
g/cm3 |
ZhongMu Method |
特性黏度-Intrinsic Viscosity |
0.50±0.02 |
dl/g |
ZhongMu Method |
分子量-Molecuar weight |
49000~57000 |
|
ZhongMu Method |
挥发物-Volatiles |
<0.5 |
% |
ZhongMu Method |
甲苯含量-Toluene Content |
<1500 |
ppm |
ZhongMu Method |
铜含量-Copper Content |
<10 |
ppm |
ZhongMu Method |
熔融指数-Melt Index |
4~10 |
( 315 ℃, 10Kg) g/10min |
ZhongMu Method |
热性能-Thermal Properties |
|
|
|
玻璃化温度-Tg (half width) |
215 |
℃ |
ZhongMu Method |
品名: | 聚苯醚(颗粒) |
---|---|
用途: | 暂无数据 |
别名 | 暂无数据 |